isothermal quenching

The mechanical properties of nodular cast iron can be further improved by isothermal quenching.

等温淬火处理可进一步提高球墨铸铁的机械性能.

The isothermal quenching process of the ductile iron camshaft was analyzed.

对球铁凸轮轴的等温淬火工艺进行了分析.

Influence of isothermal quenching after forging on impact toughness of semi-steel

锻造等温淬火对半钢的冲击韧性的影响

The good isothermal quenching process is austenitizing at 800 ℃ and thermal quenching at 280 ℃ for 3 hours.

该钢理想的等温处理工艺为800℃奥氏体化+280℃等温3h。

The experimental results indicate that during 30-120 min, with increasing the isothermal quenching time, the content and carbon content of retained austenite increased to a max value at 60 min, then decreased.

试验结果表明，在30～120min等温淬火时间范围内，随着等温淬火时间的延长，残余奥氏体量及其含碳量逐渐增加，60min时出现峰值，然后逐渐降低；